Table 2 Properties of sintered ceramic pieces and a commercial brick
From: Ceramic bricks containing Ni ions from contaminated biomass used as an adsorbent
Brick | apD (g cm−3) | apsW (g cm− 3) | apP (%) | H2OAbs (%) | apV (cm3) | LOI (%) | σstr (MPa) | MOR (MPa) |
|---|---|---|---|---|---|---|---|---|
ARC | 1.994 ± 0.001 | 1.997 ± 0.001 | 26.2 ± 0.2 | 13.1 ± 0.1 | 10.12 ± 0.06 | 8.6 ± 0.1 | 24.3 ± 0.1 | 2.8 ± 0.3 |
COM | 1.37 ± 0.01 | 1.38 ± 0.01 | 44.2 ± 0.4 | 32.15 ± 0.05 | 13 ± 1 | – | 2.9 ± 0.1 | 1.7 ± 0.1 |
AN20 | 1.854 ± 0.003 | 1.857 ± 0.003 | 31.28 ± 0.02 | 16.85 ± 0.04 | 11.242 ± 0.006 | 13.9 ± 0.9 | 10.5 ± 0.1 | 2.41 ± 0.01 |
AZ20 | 1.84 ± 0.02 | 1.85 ± 0.02 | 31.4 ± 0.7 | 17.0 ± 0.5 | 10.58 ± 0.02 | 12.4 ± 0.7 | 9.7 ± 0.1 | 1.82 ± 0.07 |